Aquaprufe PVC | Polyvinyl Chloride Membrane Keshun Waterproof Technology CKS
Aquaprufe PVC is a high-performance waterproof membrane with its core material polyvinyl chloride. During manufacture, it is added special additives and anti-aging agents before proceeding to advanced equipment and technique process. All those steps are taken results in a product with excellent tensile strength, strong elongation, small shrinkage rate, good flexibility even at low temperature and long lifespan of the product.
Aquaprufe PVC has a wide application area such as industrial waterproofing, damp proof construction, residential roof, infrastructure railway, traffic, swimming pool, water tank, and other related moisture barrier project.
Waterproofing Membrane
PVC
• Homogeneous (H) (Non-exposed)
• Homogeneous (H) (Exposed)
• With fiber backing L (Non-exposed)
• With fiber backing L (Exposed)
• In-fabric reinforcement P (Exposed)
• Customize
| Feature | Performance |
|---|---|
| Wear and Tear resistant | High tensile strength and able to elongate and maintain the same structural form even in high or low temperature |
| Easy installation | installation by just using hot welding method |
| Chemical resistant | suitable for many project site |
| High flexibility | good plasticity make it easy to operate the details |
| Specification | Properties |
|---|---|
| Max tension (N/cm)) | L : 120 P : 250 |
| Tension strength (MPa) | H : 10 |
| Max tensile elongation (%) | P : 15 |
| Elongation at break (%) | H : 200 L : 150 |
| Dimensional change after heat treatment (%) | H : 2.0 L : 1.0 P : 0.5 |
| Low temperature bending | -25°C no cracking |
| Water impermeability | 0.3 MPa, 2hr impermeable |
| Shock resistance | 0.5kg.m, no leaking |
| Anti static resistance | P : 20kg, impermeable |
| Seam peel strength (N/mm) | H : 4.0 or membrane breakage L : 4.0 or membrane breakage P : 3.0 |
| Angle tear strength (N/mm) | H : 50 |
| Trapezoidal tearing strength | L : 150 P : 250 |
| Water absorption % 70°C, 168h | After immersion : 4.0 After drying : -4.0 |
| Period (hr) | 672 |
| Exterior | No bubbling, crack, layered, bonding, and hole |
| Max tension retention rate (%) | L : 85 P : 85 |
| Tension retention rate (%) | H : 85 |
| Max elongation retention rate (%) Heat aging (80°C) | P : 80 |
| Elongation retention after tear (%) | H : 80 L : 80 |
| Low temperature bending | -20°C, no cracking |