Aquatorch Salinity | Polyester Elastomer Bitumen Membrane Keshun Waterproof Technology CKS
Aquatorch Salinity is a polyester elastomeric modified bitumen waterproof membrane. It is a specially formulated waterproof membrane for the usage of building project that exposed to sea spray or any salt aerosol area. Because building nearby require waterproofing membrane that has high salinity resistant to avoid salt water moisture or water damaged the membrane. Besides that it also good weather resistance, high tensile strength, high elongation, wear and tear resistance, and easy application. The membrane is made up of polyester felt as the base layer and the styrene butadiene styrene (SBS) with modified bitumen is used as the surface materials together with an extra salt tolerant additives.
Aquatorch Salinity is specially formulated waterproof membrane for the building project that exposed to sea spray or any salt aerosol area such as coastal area building roof, basement, tunnel, water grid system, and other projects that required saline resistant.
Waterproofing Membrane
SBS, Modified Bitumen, Polyester Felt
NA
| Feature | Performance |
|---|---|
| Weather resistant | Yes |
| Wear and Tear resistant | high elongation |
| Easy installation | Yes |
| Salt tolerance | suitable for coastal areas and high saline-alkali areas |
| Waterproof | Yes |
| Specification | Properties |
|---|---|
| Soluble matter content g/m² | Thickness 3mm : 2100 Thickness 4mm : 2900 |
| Heat Resistance | 105°≤2mm, no flow, drippage |
| Water tightness | 0.3MPa, 30 min impermeable |
| Low temperature flexibility | -25°C No crack |
| Maximum tension peak N/50mm | 800, no crack or seperating |
| Maximum elongation peak rate | ≥40 |
| Increase in mass after immersion in water % | ≤1 |
| Heat ageing | Retention rate of tension : ≥ 90 % Retention rate of elongation : ≥ 80 % Low temperature flexibility : -20°C, No crack Size change rate : ≤ 0.7 % Mass loss : ≤ 1.0 % |
| Oil permeability, number of sheets | ≤2 |
| Seam peel strength N/mm | ≥1.5 |
| Thickness of asphalt coating on lower surface of coiled material mm | ≥1.0 |
| Salt treatment (20% NaCl solution, 30D) | Tension retention rate : ≥ 90 Elongation : ≥ 80 % Low temperature bending : -23°C, No crack |
| Alkali treatment (saturated Ca(OH)2 solution, 30D) | Tension retention rate : ≥ 90 Elongation : ≥ 80 % Low temperature bending : -23°C, No crack |
| Artificial climate accelerated aging | Exterior : no slip, flow, drippage Tension retention rate : ≥ 80 % Low temperature bending : -20°C, No crack |
NA
NA
NA